Scientists in Munich Working on Perpetual Youth for Batteries

By  Tuesday, 17.11.2015, 21:17    General News

Scientists in Munich are working on ways to keep the pink rabbit running even longer. A key issue with lithium ion batteries is aging. It significantly reduces their potential storage capacity. To date, very little is known about the causes of the aging effects. Scientists from the Department of Technical Electrochemistry and the Research Neutron Source FRM II at the Technical University of Munich have now come a step closer to identifying the causes in their latest experiments.

Lithium ion batteries with graphite anodes are a relatively new development. They were patented only in 1989 and have been deployed in electrical devices since 1991. Since then, they have been a success worldwide and do their service not only in small electrical devices but also in electric cars, airplanes and even locomotives. In the future they will also serve as intermediate storage with up to megawatt capacities.

Batteries with graphite anodes suffer their first significant loss of capacity during the initial charging cycle, the formation step. A battery loses up to ten percent of its capacity in the process. Each additional charge-discharge cycle reduces storage capacity further, if only insignificantly. Capacity is also lost through the mere storage of batteries – especially above room temperature.

Physics has come up with a number of ideas about the nature of these aging effects, but no one has yet found the definitive explanation for them. TUM scientists have now come a good deal closer to closing this knowledge gap in their latest experiments.

In order to understand the aging mechanism and to uncover the reasons behind them, they combined electrochemical investigations with measurement methodologies as diverse as X-ray diffraction, impedance measurements and prompt gamma activation analysis (PGAA).

They deployed these methodologies to analyze the behavior of batteries with graphite anodes and nickel-manganese-cobalt cathodes, so-called NMC cells, at various temperatures. NMC cells are popular in electromobility since they have a large capacity and can theoretically handle charging voltages up to just under five volts. However, above 4.4 volts aging effects increase strongly.

Using X-ray diffraction, the scientists investigated the loss of active lithium over multiple charging cycles. They used impedance measurements to register the increasing resistance in the battery cells. Neutron activation analysis ultimately facilitated the accurate determination of extremely minute quantities of transition metals on the graphite electrodes.

The significant capacity loss in the formation step is caused by the build-up of a pacifying layer on the anode. This consumes active lithium, but also protects the electrolyte from decomposition at the anode.

The research group determined two key mechanisms for the loss of capacity during operation: The active lithium in the cell is slowly used up in various side reactions and is thus no longer available. The process is very temperature dependent: At 25 °C the effect is relatively weak but becomes quite strong at 60 °C.

When charging and discharging cells with a higher upper cut off potential (4.6 V), cell resistance increases rapidly. The transition metals deposited on the anode may increase the conductivity of the pacifying layer and thereby speed up the decomposition of the electrolyte.

By way of trial and error, battery manufacturers have determined the optimal relationship between the electrode material and lithium. “Using our insights, now individual processes can be improved,” says Irmgard Buchberger, PhD student at the Department of Electrochemistry at TU Munich. “Possibilities include additives that improve the build-up of the pacifying layer, for example, or modifications of the cathode surface.”


Rate this
Vilijam Zufic

Translator (German, Croatian, English), guide and unacknowledged blogging genius. Born and lives in Pula, Istria, Croatia. Educated in Germany, Croatia and the United States, economics graduate. Currently beginning to prepare to train for pulling himself up by his bootstraps. Married with children. Father of Croatia’s greatest football talent. Knows all there is to know about Istria, camping and bratwurst. At the verge of something big with the only German language blog on Istria No sense of humour. Here to meet like-minded people.

Website: Email This email address is being protected from spambots. You need JavaScript enabled to view it.
<< Expand >>
>> Collapse <<